FRACTURE ANALYSIS OF MAIN TRANSFORMER EQUIPMENT CLAMP IN NUCLEAR POWER PLANT

ZHANG HongWu; FENG NanNan; LIU Rui; CHEN Yang

doi:10.16579/j.issn.1001.9669.2022.05.012

您当前的位置：

首页 >

文章列表页 >

FRACTURE ANALYSIS OF MAIN TRANSFORMER EQUIPMENT CLAMP IN NUCLEAR POWER PLANT

更新时间：2022-11-10

- FRACTURE ANALYSIS OF MAIN TRANSFORMER EQUIPMENT CLAMP IN NUCLEAR POWER PLANT
- Journal of Mechanical Strength Vol. 44, Issue 5, Pages: 1101-1106(2022)
- 作者机构：
  
  1. 山东电力工业锅炉压力容器检验中心有限公司
  2. 国网山东省电力公司电力科学研究院
  3. 济南经纬电力工程咨询有限公司
  4. 国网山东省电力公司经济技术研究院
- 作者简介：
- 基金信息：
- DOI：10.16579/j.issn.1001.9669.2022.05.012
  CLC：
扫描看全文
ZHANG HongWu, FENG NanNan, LIU Rui, et al. FRACTURE ANALYSIS OF MAIN TRANSFORMER EQUIPMENT CLAMP IN NUCLEAR POWER PLANT. [J]. 44(5):1101-1106(2022)
DOI：

ZHANG HongWu, FENG NanNan, LIU Rui, et al. FRACTURE ANALYSIS OF MAIN TRANSFORMER EQUIPMENT CLAMP IN NUCLEAR POWER PLANT. [J]. 44(5):1101-1106(2022) DOI： 10.16579/j.issn.1001.9669.2022.05.012.

摘要

某核电站主变压器的多个设备线夹发生了断裂。对断裂的设备线夹以及同批次的备品设备线夹取样，通过宏观检验、渗透检测、金相分析、断口微观形貌分析、压接质量检测、导电率检测和XRD检测，对断裂原因进行了分析。断裂产生的主要原因是设备线夹在强度不足且性能下降的情况下承受了各方面应力，最终在焊缝最薄弱处产生裂纹，形成断裂。为避免同类事故的发生，建议加强金属监督，严把设备质量关。

Abstract

Several equipment clamps of main transformer in a nuclear power company were broken. Taking samples from the broken equipment clamps and the same batch of spare equipment clamps, the fracture causes were analyzed through macroscopic inspection, penetrant testing, metallographic analysis, micro morphology testing, crimping quality testing, conductivity testing and XRD testing. The main reason for the fracture is that the equipment clamp bears all kinds of stress under the condition of insufficient strength and performance degradation, and finally cracks appear at the weakest part of the weld, forming fracture. In order to avoid the occurrence of similar accidents, it is suggested to strengthen the metal supervision and strictly control the quality of the access equipment.

关键词

设备线夹强度不足性能下降最薄弱处断裂金属监督

Keywords

Equipment clampInsufficient strengthPerformance degradationWeakest pointFractureMetal supervision

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

FATIGUE TEST AND CRACK PROPAGATION SIMULATION OF THE SMALL WELDED PIPE

ANALYSIS METHOD ON STRESS INTENSITY FACTOR FOR CRACKED 60 DEGREE THIN-WALL EQUILATERAL ANGLE STEEL

STRESS INTENSITY FACTORS FOR CIRCUMFERENTIAL PERIODIC CRACKED PIPES UNDER BENDING

FRACTURE FAILURE ANALYSIS OF A AUTO HIGH STRENGTH ASSEMBLING BOLT

DAMAGE PARAMETERS IDENTIFICATION OF ALUMINUM ALLOY BASED ON ANISOTROPIC GTN MODEL

Related Author

No data

Related Institution

Suzhou Nuclear Power Research Institute

Science and Technology on Liquid Rocket Engine Laboratory

Department of Mining Engineering,Liaoning Shihua University

Department of Mechanical Engineering,Liaoning University of Petroleum ＆ Chemical Technology

Department of Mechanical Engineering,Chongqing Industry Polytechnic College

⁰