FATIGUE FRACTURE ANALYSIS OF BRASS OSCILLATOR WIRE OF VERTICAL LOG-PERIODIC ANTENNAZHENG DEZHI SONG ZONGFENG LIANG HANXIN

ZHENG DeZhi; SONG ZongFeng; LIANG HanXin

doi:10.16579/j.issn.1001.9669.2021.05.026

您当前的位置：

首页 >

文章列表页 >

FATIGUE FRACTURE ANALYSIS OF BRASS OSCILLATOR WIRE OF VERTICAL LOG-PERIODIC ANTENNAZHENG DEZHI SONG ZONGFENG LIANG HANXIN

更新时间：2022-09-22

- FATIGUE FRACTURE ANALYSIS OF BRASS OSCILLATOR WIRE OF VERTICAL LOG-PERIODIC ANTENNAZHENG DEZHI SONG ZONGFENG LIANG HANXIN
- Journal of Mechanical Strength Vol. 43, Issue 5, Pages: 1206-1212(2021)
- 作者机构：
  
  1. 中国电波传播研究所
- 作者简介：
- 基金信息：
- DOI：10.16579/j.issn.1001.9669.2021.05.026
  CLC：
扫描看全文
ZHENG DeZhi, SONG ZongFeng, LIANG HanXin. FATIGUE FRACTURE ANALYSIS OF BRASS OSCILLATOR WIRE OF VERTICAL LOG-PERIODIC ANTENNAZHENG DEZHI SONG ZONGFENG LIANG HANXIN. [J]. 43(5):1206-1212(2021)
DOI：

ZHENG DeZhi, SONG ZongFeng, LIANG HanXin. FATIGUE FRACTURE ANALYSIS OF BRASS OSCILLATOR WIRE OF VERTICAL LOG-PERIODIC ANTENNAZHENG DEZHI SONG ZONGFENG LIANG HANXIN. [J]. 43(5):1206-1212(2021) DOI： 10.16579/j.issn.1001.9669.2021.05.026.

摘要

架设在北方某地区的垂直对数周期天线,在2018年出现了振子线的断裂现象,主要对振子线的断裂原因进行分析。通过对黄铜材料断裂的两种可能性进行分析,得出黄铜振子线断裂原因为疲劳损伤。造成疲劳损伤的原因主要有,对大吊索进行了拉紧调整及当地的温差较大,导致振子线的应力远超出原始设计时的应力。根据振子线断裂原因,提出了改进方案,以满足该地区对该天线的使用要求。

Abstract

The fracture reason analysis of oscillator wire was performed of vertical log-periodic antenna,which mounted somewhere in the north of China in 2018. Through the analysis of two possibilities of brass material fracture,the results show the reason of brass oscillator wire fracture is fatigue damage. The main causes of fatigue damage are the tension adjustment of the antenna cable and the large local temperature difference,which results in the stress of the oscillator wire far exceeding the original design stress. According to the reason breakage of the brass oscillator wire,an improved scheme is proposed to meet the antenna requirements in this area.

关键词

垂直对数周期天线大吊索黄铜振子线断裂分析疲劳损伤

Keywords

Vertical log-periodic antennaCableBrass oscillator wireFracture analysisFatigue damage

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

LIFE PREDICTION OF METRO OBSTACLE DETECTOR BASED ON FATIGUE TEST AND FRACTURE SIMULATION

RESEARCH ON THE RELATIONSHIP BETWEEN LOAD ANALYSIS METHOD AND FATIGUE OF LOWER CONTROL ARM

FRACTURE ANALYSIS AND IMPROVEMENT OF EGR COOLER WITH ECCENTRIC INTAKE STRUCTURE

RESEARCH ON THE CONTACT STRESS OF ROLLS AND FATIGUE DAMAGE DISTRIBUTION OF BACKUP ROLL IN FOUR HIGH PC MILL

FATIGUE ANALYSIS OF PITCH BEARING AND HUB CONNECTION BOLT IN MEGAWATT WIND TURBINE

Related Author

No data

Related Institution

Traction Power State Key Laboratory,Southwest Jiaotong University

Hebei Key Laboratory of Special Delivery Equipment,Yanshan University

Chongqing Automotive Chassis Research Engineering Center

China Automotive Engineering Research Institute Co.,Ltd.

Zhejiang Bondlye Environmental Technology Co.,Ltd.

⁰