STUDY ON FATIGUE PERFORMANCE OF CRACKED STEEL STRUCTURE REPAIRED WITH STOP-HOLE AND CFRP

HUANG ChuanHai; LIU ZhiPing

doi:10.16579/j.issn.1001.9669.2021.02.024

您当前的位置：

首页 >

文章列表页 >

STUDY ON FATIGUE PERFORMANCE OF CRACKED STEEL STRUCTURE REPAIRED WITH STOP-HOLE AND CFRP

更新时间：2022-09-22

- STUDY ON FATIGUE PERFORMANCE OF CRACKED STEEL STRUCTURE REPAIRED WITH STOP-HOLE AND CFRP
- Journal of Mechanical Strength Vol. 43, Issue 2, Pages: 418-424(2021)
- 作者机构：
  
  1. 武汉理工大学物流工程学院
  2. 港口物流技术与装备教育部工程研究中心
- 作者简介：
- 基金信息：
- DOI：10.16579/j.issn.1001.9669.2021.02.024
  CLC：
扫描看全文
HUANG ChuanHai, LIU ZhiPing. STUDY ON FATIGUE PERFORMANCE OF CRACKED STEEL STRUCTURE REPAIRED WITH STOP-HOLE AND CFRP. [J]. 43(2):418-424(2021)
DOI：

HUANG ChuanHai, LIU ZhiPing. STUDY ON FATIGUE PERFORMANCE OF CRACKED STEEL STRUCTURE REPAIRED WITH STOP-HOLE AND CFRP. [J]. 43(2):418-424(2021) DOI： 10.16579/j.issn.1001.9669.2021.02.024.

摘要

起重机金属结构在长期服役过程中易产生疲劳裂纹,使用止裂孔与碳纤维复合材料(CFRP)对含疲劳裂纹的金属结构进行复合修复能获得比单一修复方式更好的效果。针对复合修复后止裂孔边缘裂纹萌生阶段,使用Abaqus与Fe-Safe建立有限元分析模型,分析了加固方式、止裂孔半径、疲劳裂纹长度及裂纹尖端到止裂孔边缘的距离等因素对裂纹萌生寿命的影响,并通过试验进行了验证。结果表明,利用Abaqus与Fe-Safe对复合修复后的结构进行耐久性分析具有可行性,能够为制定修复方案提供参考。

Abstract

For crane metal constructions,fatigue cracks during long-term services easily occurs. A combination of crack stop-hole and CFRP for repairing cracked metal structures can achieve better results than single repairing methods. For the crack initiation stage of the crack stop-hole edge after composite repair,by utilizing ABAQUS and FE-SAFE to establish a finite element analysis model,the influence of factors such as the reinforcement method,the radius of the stop-hole,the length of the fatigue crack and the distance from the crack tip to the edge of the crack stop on the crack initiation life were analyzed and verified through experiments. The results show that it is feasible to use ABAQUS and FE-SAFE to analyze the durability of the composite repaired structure,which can provide references for the formulation of plans to repair.

关键词

碳纤维复合材料止裂孔复合修复裂纹萌生疲劳分析

Keywords

Carbon fiber reinforced polymer（CFRP）Crack stop-holeComposite repairCrack initiationFatigue analysis

references

Views

179

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

SIMULATION OF FATIGUE CRACK INITIATION LIFE OF TC4 TITANIUM ALLOY BASED ON ITS MESOSCOPIC PROPERTIES

STUDY ON THE CHARACTERISTICS OF MICRO-PITTING DAMAGES FOR HIGH POWER DENSITY GEAR TRANSMISSION

DYNAMIC LOAD SIMULATION OF 4WD SUV AND FATIGUE LIFE ANALYSIS OF FRAME

THERMAL STRESS ANALYSIS AND FATIGUE CHECK OF MAIN STEAM SAFETY VALVE FOR NUCLEAR POWER STATIONS

SIMULATION AND ANALYSIS OF CRACKING EXHAUST PIPE FOR SINGLE-CYLINDER DIESEL ENGINE

Related Author

No data

Related Institution

AVIC Shenyang Aircraft Design ＆ Research Institute

State Key Laboratory of Mechanics and Control of Mechanical Structures,Nanjing University of Aeronautics and Astronautics

Pump Branch,CNPC Baoji Oilfield Machinery Co.,Ltd.

R ＆ D Center,Zhengzhou Research Institute of Mechanical Engineering Co.,Ltd.

Product Development ＆ Technical Center Jiangling Motors Co,Ltd.

⁰