REASEARCH ON HIGH ENERGY DENSITY PULSE CURRENT REDUCTION RESIDUAL STRESS IN Cr12MoV STEEL QUENCHING SPECIMEN

WANG SiQi; GU BangPing; HU Xiong; XU GuanHua; WANG Ping; ZHUANG JiaYi; WU ChenYu

doi:10.16579/j.issn.1001.9669.2020.06.011

您当前的位置：

首页 >

文章列表页 >

REASEARCH ON HIGH ENERGY DENSITY PULSE CURRENT REDUCTION RESIDUAL STRESS IN Cr12MoV STEEL QUENCHING SPECIMEN

更新时间：2022-09-22

- REASEARCH ON HIGH ENERGY DENSITY PULSE CURRENT REDUCTION RESIDUAL STRESS IN Cr12MoV STEEL QUENCHING SPECIMEN
- Journal of Mechanical Strength Vol. 42, Issue 6, Pages: 1343-1347(2020)
- 作者机构：
  
  1. 上海海事大学物流工程学院
  2. 浙江大学浙江省先进制造技术重点实验室
- 作者简介：
- 基金信息：
- DOI：10.16579/j.issn.1001.9669.2020.06.011
  CLC：
扫描看全文
WANG SiQi, GU BangPing, HU Xiong, et al. REASEARCH ON HIGH ENERGY DENSITY PULSE CURRENT REDUCTION RESIDUAL STRESS IN Cr12MoV STEEL QUENCHING SPECIMEN. [J]. 42(6):1343-1347(2020)
DOI：

WANG SiQi, GU BangPing, HU Xiong, et al. REASEARCH ON HIGH ENERGY DENSITY PULSE CURRENT REDUCTION RESIDUAL STRESS IN Cr12MoV STEEL QUENCHING SPECIMEN. [J]. 42(6):1343-1347(2020) DOI： 10.16579/j.issn.1001.9669.2020.06.011.

摘要

针对淬火工艺导致材料表面引入较大残余压应力的问题,采用高能量密度脉冲电流的方法消减淬火Cr12MoV钢残余应力。采用不同密度的脉冲电流对试样进行处理,并采用小孔法和硬度测试法分析脉冲电流处理前后材料的残余应力和表面硬度,在此基础上建立电致塑性模型框架阐述脉冲电流对残余应力和表面硬度的作用机理。结果表明:高能量密度脉冲电流能够有效地消减Cr12MoV钢淬火残余应力,且在一定范围内提高脉冲电流的密度可以提高残余应力的消减效果;淬火Cr12MoV钢表面硬度从HRC 61～HRC 64降低到HRC 56～HRC 59;位错密度的减小是残余应力释放和表面硬度降低的本质原因。高能量密度脉冲电流能够被用来消减淬火工艺引起的残余应力,提高零件的使用寿命,具有一定的工程应用价值。

Abstract

Aiming at the problem of introducing large residual compressive stress on the surface of the material due to the quenching process,the high energy density electric current pulse（ECP） technology was introduced to reduce the residual stress in Cr12 MoV steel.The samples were treated with different density ECP and the residual stress and surface hardness of the materials before and after ECP were analyzed by the hole-drilling method and hardness test method.Based on this,an electroplastic model framework was established to explain the mechanism of ECP on residual stress and surface hardness.The results show that high energy density ECP can effectively eliminate the residual stress of quenched Cr12 MoV steel,and increasing the density of the ECP within a certain range can improve the residual stress reduction effect; Surface hardness of quenched Cr12 MoV steel decreased from 61 HRC～64 HRCto 56 HRC～59 HRC;The reduction in dislocation density is an essential cause of residual stress release and surface hardness reduction.The high energy density ECP can be used to reduce the residual stress caused by the quenching process and improve the service life of the parts,which has certain engineering application value.

关键词

脉冲电流Cr12MoV钢残余应力表面硬度电致塑性

Keywords

Pulse currentCr12MoV steelResidual stressSurface HardnessElectroplasticity

references

Views

133

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

STUDY ON THE EFFECT OF ROLLING STRENGTHENING ON THE SURFACE INTEGRITY OF 45 STEEL THREAD ROOT

STUDY ON LIFE PREDICTION AND FATIGUE TEST OF ZM6 MATERIAL WITH IMPACT PIT

RESEARCH ON STRESS AND PRECISION CONTROL TECHNOLOGY OF WELDED STEEL PARTS

RESEARCH ON THE RESIDUAL STRESS OF THE CRYSTAL SURFACE DURING LAPPING PROCESS BASED ON A SINGLE PARTICLE MODEL

TESTING RESEARCH OF STRESS AND DEFORMATION OF WELDED STRUCTURE BODY

Related Author

No data

Related Institution

Henan Province Industrial Technology Research Institute of Resources and Materials,Zhengzhou University

School of Mechanical and Power Engineering,Zhengzhou University

School of Aeronautic Science and Engineering, Beihang University

AECC Hunan Aviation Powerplant Research Institute

China Academy of Machinery Science and Technology Group Co.,Ltd.

⁰