TESTING RESEARCH OF STRESS AND DEFORMATION OF WELDED STRUCTURE BODY

WEI DongHai; LI KeRui; DU Bing; CHENG Peng

doi:10.16579/j.issn.1001.9669.2020.04.027

您当前的位置：

首页 >

文章列表页 >

TESTING RESEARCH OF STRESS AND DEFORMATION OF WELDED STRUCTURE BODY

更新时间：2022-09-22

- TESTING RESEARCH OF STRESS AND DEFORMATION OF WELDED STRUCTURE BODY
- Journal of Mechanical Strength Vol. 42, Issue 4, Pages: 931-936(2020)
- 作者机构：
  
  1. 郑州机械研究所有限公司
  2. 机械科学研究总院集团有限公司
- 作者简介：
- 基金信息：
- DOI：10.16579/j.issn.1001.9669.2020.04.027
  CLC：
扫描看全文
WEI DongHai, LI KeRui, DU Bing, et al. TESTING RESEARCH OF STRESS AND DEFORMATION OF WELDED STRUCTURE BODY. [J]. 42(4):931-936(2020)
DOI：

WEI DongHai, LI KeRui, DU Bing, et al. TESTING RESEARCH OF STRESS AND DEFORMATION OF WELDED STRUCTURE BODY. [J]. 42(4):931-936(2020) DOI： 10.16579/j.issn.1001.9669.2020.04.027.

摘要

采用盲孔法和数字水平仪分别测试了焊接床身的焊后初始残余应力和变形,以及振动时效、热时效、抛丸处理后的应力和加工后的变形。结果表明:焊接床身的初始残余应力可高达300.6 MPa,导轨变形量最大为2 882.07μm,有明显的变形;采用复合时效处理后的两件焊接床身的最大拉应力分别降低至43.8 MPa和12.1 MPa,均低于50 MPa;加工后导轨的最大直线度降低至26.7μm和23.6μm,明显减小。

Abstract

The initial residual stress and deformation of welded body was measured respectively with blind-hole method and digital level. The test of residual stress after vibration aging,thermal aging and shot peening and the test of deformation after processing were done. The results show that the initial residual stress of welded body can reach up to 300. 6 MPa. The maximum deformation of the guide rails is 2882. 07 μm,which means obvious deformation. After complex aging process,the maximum residual stress of two welded bodys respectively is reduced to 43. 8 MPa and 12. 1 MPa,which both below 50 MPa. After processing,the maximum straightness of the guide rail respectively is 26. 7 μm and 25. 4 μm,which is significantly reduced.

关键词

焊接床身残余应力热时效振动时效抛丸直线度

Keywords

Welding lathe bodyResidual stressHeat agingVibration agingShot peeningStraightness

references

Views

117

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

RESEARCH ON STRESS AND PRECISION CONTROL TECHNOLOGY OF WELDED STEEL PARTS

STUDY ON THE EFFECT OF ROLLING STRENGTHENING ON THE SURFACE INTEGRITY OF 45 STEEL THREAD ROOT

STUDY ON LIFE PREDICTION AND FATIGUE TEST OF ZM6 MATERIAL WITH IMPACT PIT

RESEARCH ON THE RESIDUAL STRESS OF THE CRYSTAL SURFACE DURING LAPPING PROCESS BASED ON A SINGLE PARTICLE MODEL

REASEARCH ON HIGH ENERGY DENSITY PULSE CURRENT REDUCTION RESIDUAL STRESS IN Cr12MoV STEEL QUENCHING SPECIMEN

Related Author

No data

Related Institution

Henan Province Industrial Technology Research Institute of Resources and Materials,Zhengzhou University

School of Mechanical and Power Engineering,Zhengzhou University

School of Aeronautic Science and Engineering, Beihang University

AECC Hunan Aviation Powerplant Research Institute

Sichuan Branch,China Classification Society Certification Company

⁰