FRACTURE ANALYSIS AND IMPROVEMENT OF BALL SCREW STEPPED SHAFT

NIE QingFeng; YU DongHui; LI HaiHong

doi:10.16579/j.issn.1001.9669.2018.03.038

您当前的位置：

首页 >

文章列表页 >

FRACTURE ANALYSIS AND IMPROVEMENT OF BALL SCREW STEPPED SHAFT

更新时间：2022-09-22

- FRACTURE ANALYSIS AND IMPROVEMENT OF BALL SCREW STEPPED SHAFT
- Journal of Mechanical Strength Vol. 40, Issue 3, Pages: 745-748(2018)
- 作者机构：
  
  1. 中国空空导弹研究院
- 作者简介：
- 基金信息：
- DOI：10.16579/j.issn.1001.9669.2018.03.038
  CLC：
扫描看全文
NIE QingFeng, YU DongHui, LI HaiHong. FRACTURE ANALYSIS AND IMPROVEMENT OF BALL SCREW STEPPED SHAFT. [J]. 40(3):745-748(2018)
DOI：

NIE QingFeng, YU DongHui, LI HaiHong. FRACTURE ANALYSIS AND IMPROVEMENT OF BALL SCREW STEPPED SHAFT. [J]. 40(3):745-748(2018) DOI： 10.16579/j.issn.1001.9669.2018.03.038.

摘要

针对某伺服系统在加载试验后滚珠丝杠副丝杠台阶轴断裂的情况,从硬度偏高、材料缺陷、加工工艺以及使用加载情况等方面对故障现象进行了分析和计算,最终确定断裂原因为电火花加工导致丝杠表面处于拉应力状态且存在许多微观裂纹,加之台阶轴内部螺纹锈蚀降低了承载面积,二者综合导致了零件的扭转断裂。针对该故障原因,给出了控制电火花加工规范、增加研磨和抛光等改进措施。

Abstract

The stepped shaft of ball screw was breakaway after loading test of transmission mechanism. To solve this problem,analysis and calculations were carried out from higher hardness,material defect,machining process and experimental loading. The results show that electro discharge machining（ EDM） causes tensile stress and microcosmic cracks on the surface microstructure. Meanwhile,thread corrosion of stepped shaft reduces the loaded area. As a result,torsional fracture of the stepped shaft happened. According to the result,improvement measures including process criterion of EDM control,grinding and polishing are proposed.

关键词

滚珠丝杠副台阶轴断裂

Keywords

Ball ScrewStepped shaftFracture

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

FRACTURE ANALYSIS OF MAIN TRANSFORMER EQUIPMENT CLAMP IN NUCLEAR POWER PLANT

FATIGUE TEST AND CRACK PROPAGATION SIMULATION OF THE SMALL WELDED PIPE

ANALYSIS METHOD ON STRESS INTENSITY FACTOR FOR CRACKED 60 DEGREE THIN-WALL EQUILATERAL ANGLE STEEL

STRESS INTENSITY FACTORS FOR CIRCUMFERENTIAL PERIODIC CRACKED PIPES UNDER BENDING

FRACTURE FAILURE ANALYSIS OF A AUTO HIGH STRENGTH ASSEMBLING BOLT

Related Author

No data

Related Institution

State Grid Shandong Electric Power Economic ＆ Technology Research Institute

Jinan Jingwei Electric Power Engineering Consulting Co.,Ltd.

State Grid Shandong Electric Power Research Institute

Shandong Electric Power Industry Boiler and Pressure Vessel Inspection Center Co.,Ltd.

Science and Technology on Liquid Rocket Engine Laboratory

⁰