LOW CYCLE FATIGUE LIFE PREDICTIONS OF 15CrMoR PARENT MATERIAL AND WELD METAL

MA Kai; WANG ChuanZhi; DONG JunHua; GAO BingJun

doi:10.16579/j.issn.1001.9669.2016.04.007

您当前的位置：

首页 >

文章列表页 >

LOW CYCLE FATIGUE LIFE PREDICTIONS OF 15CrMoR PARENT MATERIAL AND WELD METAL

更新时间：2022-09-22

- LOW CYCLE FATIGUE LIFE PREDICTIONS OF 15CrMoR PARENT MATERIAL AND WELD METAL
- Journal of Mechanical Strength Vol. 38, Issue 4, Pages: 703-710(2016)
- 作者机构：
  
  1. 河北工业大学化工学院
  2. 北京燕华建筑安装工程有限责任公司设备制造公司
- 作者简介：
- 基金信息：
- DOI：10.16579/j.issn.1001.9669.2016.04.007
  CLC：
扫描看全文
MA Kai, WANG ChuanZhi, DONG JunHua, et al. LOW CYCLE FATIGUE LIFE PREDICTIONS OF 15CrMoR PARENT MATERIAL AND WELD METAL. [J]. 38(4):703-710(2016)
DOI：

MA Kai, WANG ChuanZhi, DONG JunHua, et al. LOW CYCLE FATIGUE LIFE PREDICTIONS OF 15CrMoR PARENT MATERIAL AND WELD METAL. [J]. 38(4):703-710(2016) DOI： 10.16579/j.issn.1001.9669.2016.04.007.

摘要

制作了焦炭塔用材15Cr MoR的对接试件,对其母材区及焊缝区金属进行了不同温度的单轴拉伸试验与全寿命单轴棘轮效应试验。利用OW-II随动强化模型对材料的棘轮效应进行预测,模型能较好地预测材料稳定段的棘轮应变率。通过单轴拉伸试验数据得出预测低周疲劳寿命的基本参数,选用考虑棘轮效应的MSRS模型对母材区焊缝区材料疲劳寿命进行预测,预测结果均在2倍误差带以内,而且预测结果均匀分布在45°精确线两侧。利用OW-II随动强化模型在相同工况下预测出的母材区焊缝区稳定段棘轮应变率,应变幅值,带入MSRS模型,预测结果表明母材区疲劳寿命明显低于焊缝区,稳定段棘轮应变率母材区明显高于焊缝区。

Abstract

Butt-weld specimen has been made for coke drum material 15 Cr MoR. For both parent and weld materials,uniaxial tensile tests and uniaxial ratcheting tests have been conducted under different temperatures. The OW-II kinematic hardening constitutive model has been used to predict the material ratcheting effect using the experimental data obtained. Test results show that the OW-II model can well predict ratcheting strain rates for the stable period. Based on the obtained uniaxial tensile test data,basic parameters for predicting low cycle fatigue life have been obtained. The MSRS model has been used to predict the fatigue lives of the parent material and weld metal. The predicted results are within the 2 times error band and are uniformly distributed on both sides of 45 ° line accurately. Furthermore,the ratcheting strain rate and the strain amplitude for the stable period are obtained for the parent metal and the weld metal respectively by the OW-II kinematic hardening constitutive model under the same conditions. The MSRS model predicts that the fatigue life of the parent material is significantly lower than that of the weld metal and during the stable period the ratcheting strain rate of parent material is significantly higher than that of the weld metal.

关键词

15CrMoR棘轮效应低周疲劳寿命预测

Keywords

15CrMoRRatchetingLow-cycle fatigueLife prediction

references

Views

115

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

LOW CYCLE FATIGUE LIFE PREDICTION METHOD FOR SINGLE CRYSTAL NICKEL-BASE SUPERALLOYS AT HIGH TEMPERATURE

LIFE PREDICTION OF METRO OBSTACLE DETECTOR BASED ON FATIGUE TEST AND FRACTURE SIMULATION

THERMAL-MECHANICAL FATIGUE PREDICTION OF ENGINE CYLINDER HEAD BASED ON THE SEHITOGLU MODEL

LIFE PREDICTION OF ROLLING BEARING BASED ON BIDIRECTIONAL STACKING SIMPLE RECURRENT UNIT

FATIGUE LIFE PREDICTION METHODOLOGY BASED ON WEIGHT-AVERAGED MAXIMUM SHEAR STRESS PLANE UNDER MULTIAXIAL LOADING

Related Author

No data

Related Institution

Department of Thermal Engineering,Tsinghua University

Traction Power State Key Laboratory,Southwest Jiaotong University

Tianjin Key laboratory of Power Transmission and Safety Technology for New Energy Vehicles

School of Mechanical Engineering, Hebei University of Technology

Powertrain Engineering Department,Jiangling Motors Corporation

⁰