EXPERIMENTAL STUDY ON FRACTURE PERFORMANCES OF AA LY12CZ AND FSW JOINTS

ZHANG HaiYing; LIU XiuLi; ZANG WeiFeng; DONG DengKe

doi:10.16579/j.issn.1001.9669.2015.05.007

您当前的位置：

首页 >

文章列表页 >

EXPERIMENTAL STUDY ON FRACTURE PERFORMANCES OF AA LY12CZ AND FSW JOINTS

更新时间：2022-09-22

- EXPERIMENTAL STUDY ON FRACTURE PERFORMANCES OF AA LY12CZ AND FSW JOINTS
- Journal of Mechanical Strength Vol. 37, Issue 5, Pages: 834-838(2015)
- 作者机构：
  
  1. 中国飞机强度研究所一室
- 作者简介：
- 基金信息：
- DOI：10.16579/j.issn.1001.9669.2015.05.007
  CLC：
扫描看全文
ZHANG HaiYing, LIU XiuLi, ZANG WeiFeng, et al. EXPERIMENTAL STUDY ON FRACTURE PERFORMANCES OF AA LY12CZ AND FSW JOINTS. [J]. 37(5):834-838(2015)
DOI：

ZHANG HaiYing, LIU XiuLi, ZANG WeiFeng, et al. EXPERIMENTAL STUDY ON FRACTURE PERFORMANCES OF AA LY12CZ AND FSW JOINTS. [J]. 37(5):834-838(2015) DOI： 10.16579/j.issn.1001.9669.2015.05.007.

摘要

结合多年断裂韧性测试试验的经验,研究了较薄板材C(T)试验件测定KR曲线和断裂韧性的注意事项。通过试验测定了LY12CZ铝合金及其搅拌摩擦焊接接头的KR曲线和断裂韧性,并通过金相显微镜对焊接接头的显微组织进行了观察。试验结果表明,由于焊缝中心处的致密再结晶微观组织,搅拌摩擦焊接接头的断裂韧性明显高于母材,且裂纹垂直于板材轧制方向的母材和焊接接头试验件,断裂韧性均高于裂纹平行于板材轧制方向的试验件。此外,试验结果表明C(T)试验件的断裂韧性值与面内尺寸有关,尺寸越大,断裂韧性值越高。

Abstract

Based on years’ experience in fracture toughness tests,the matters need attention for KRcurve and fracture toughness determination using thin compact tension（ C（ T）） specimen were studied.The KRcurve and fracture toughness of LY12 CZ alloy and friction stir welded joints were determined according to proposed test method.The microstructures of FSW joint were also observed utilizing metalloscope.The test result demonstrates that the fracture toughness of friction stir welded LY12 CZ alloy is higher than that of the parent alloy,because the weld nugget presents fine recrystallized structure.It is also found that the fracture toughnesses with crack perpendicular to rolling direction are higher than those with crack parallel to rolling direction for both welded and parent alloy.In addition,the test result indicates that the fracture toughness of C（ T） specimen is related to inplane dimension,and that the fracture toughness increases with the increase of in-plane dimension.

关键词

LY12CZ铝合金KR曲线断裂韧性搅拌摩擦焊C(T)试验件

Keywords

LY12CZ alloyKRcurveFracture toughnessFriction stir weldCompact tension specimen

references

Views

120

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

COMPARISON OF DIFFERENT THERMAL AGING PREDICTION MODELS OF CAST AUSTENITIC STAINLESS STEEL

STUDY ON THE DETERMINATION METHOD OF CONSTRAINT DEPENDENT FRACTURE TOUGHNESS OF STRUCTURE

EXPERIMENTAL STUDY ON J-INTEGRAL VALUE FOR THREE-POINT BEND SPECIMEN

UNIFIED CORRELATION OF GEOMETRY CONSTRAINT WITH FRACTURE TOUGHNESS FOR THE INTERFACE CRACK IN BIMETALLIC JOINTS

EXPERIMENTAL STUDY ON FRACTURE TOUGHNESS OF MULTILAYER WELD JOINT BASED ON MICROSTRUCTURE

Related Author

No data

Related Institution

Suzhou Nuclear Power Research Institute

China Nuclear Power Engineering Co., Ltd

Institute of Chemical Machinery ＆ Process Equipment,School of Energy and Power Engineering,University of Shanghai for Science and Technology

Anshan Iron ＆ Steel Group Corporation Technology Center

MOE Key Laboratory of Safety Science of Pressurized System,School of Mechanical and Power Engineering,East China University of Science and Technology

⁰