FRACTURE MECHANISM ANALYSIS AND IMPROVEMENT DESIGN OF M-PRESSURE PUMP CRANKSHAFT

DAI JieTao; LI LieJun; ZHANG ZuJiang

doi:10.16579/j.issn.1001.9669.2015.04.023

您当前的位置：

首页 >

文章列表页 >

FRACTURE MECHANISM ANALYSIS AND IMPROVEMENT DESIGN OF M-PRESSURE PUMP CRANKSHAFT

更新时间：2022-09-22

- FRACTURE MECHANISM ANALYSIS AND IMPROVEMENT DESIGN OF M-PRESSURE PUMP CRANKSHAFT
- Journal of Mechanical Strength Vol. 37, Issue 4, Pages: 761-764(2015)
- 作者机构：
  
  1. 华南理工大学机械与汽车工程学院
  2. 宝钢集团广东韶关钢铁有限公司
- 作者简介：
- 基金信息：
- DOI：10.16579/j.issn.1001.9669.2015.04.023
  CLC：
扫描看全文
DAI JieTao, LI LieJun, ZHANG ZuJiang. FRACTURE MECHANISM ANALYSIS AND IMPROVEMENT DESIGN OF M-PRESSURE PUMP CRANKSHAFT. [J]. 37(4):761-764(2015)
DOI：

DAI JieTao, LI LieJun, ZHANG ZuJiang. FRACTURE MECHANISM ANALYSIS AND IMPROVEMENT DESIGN OF M-PRESSURE PUMP CRANKSHAFT. [J]. 37(4):761-764(2015) DOI： 10.16579/j.issn.1001.9669.2015.04.023.

摘要

为了解决M型高压水泵曲轴断裂的问题,在对M泵曲轴断裂情况进行充分分析的基础上,应用Ansys有限元对曲轴进行了受力分析,通过仿真分析发现其应力集中严重的部位与断裂部位重合,同时根据实际的断裂情况对曲轴倒角的设计进行了仿真计算,重新确定了倒角的大小。为了进一步验证断裂的情况,应用解析法对其断裂截面的疲劳强度进行了校核计算,计算结果表明,原4 mm倒角情况下曲轴的疲劳强度安全系数低于许用安全系数,改进为8 mm倒角后疲劳强度安全系数满足设计要求。在此基础上对M泵的曲轴进行了改进设计,改进后的应用效果显著,解决了困扰企业的曲轴断裂问题。

Abstract

In order to solve the problems of M-pressure pump crankshaft fracture,full analysis of the M-pump caranshaft fracture was congducted. On this basis,stress analysis was carried out on the crankshaft by ANSYS. Through simulation analysis found that severe stress concentration sites coincide with the cleavage site,and conducted a simulation influence on the fracture of the crankshaft chamfer,and re-determine the size of the chamfer. To further verify the situation fracture,the fatigue strenth of frature section were checking calculation by analtical method. The results show,fatigue strength safety factor below allowable safety factor under the original conditions of the crankshaft 4mm chamfer,and fatigue strength safety factor to meet the design requirements in the case of 8mm chamfer. Improved design was performed according to the results of the simulation and calculation of the crankshaft,and applications significant effect,solved the problem of crankshaft fracture.

关键词

曲轴断裂倒角Ansys疲劳强度

Keywords

Crankshaft fractureChamferANSYSFatigue strength

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

ANALYSIS OF LOAD-BEARING MESHING CHARACTERISTICS OF CYCLOIDAL PINWHEEL OF RV REDUCER BASED ON FINITE ELEMENT MODELING (MT)

STUDY ON STRENGTH CONSTRAINTS OF OPTIMIZATION OF GEARBOX BASED ON FATIGUE THEORY

ANALYSIS FOR SOLENOID VALVE FAILURE BASED ON MULTI-PHYSICS FINITE ELEMENT MODEL

THERMAL STRESS ANALYSIS AND FATIGUE CHECK OF MAIN STEAM SAFETY VALVE FOR NUCLEAR POWER STATIONS

INFLUENCE STUDY ON THE LOGO OF AN ENGINE CONNECTING ROD TO ITS FATIGUE STRENGTH

Related Author

No data

Related Institution

Hebei Key Laboratory of Robot Sensing and Human-Robot Integration, School of Mechanical Engineering,Hebei University of Technology

State Key Laboratory of Reliability and Intelligence of Electrical Equipment, Hebei University of Technology

College of Mechanical Engineering, University of Shanghai for Science and Technology

College of Aerospace Engineering,Air Force Engineering University

China National Nuclear Corporation,CNNC

⁰